Vermiculite Coated Welding Blanket
(Ceramic Vermiculite Cloth)

Vermiculite Coated Welding Blanket

Ceramic Vermiculite Coated Inside S.S. Wire {304} Fire Blanket Details: DARSHAN SAFETY ZONE "Signature" {An ISO 9001 : 2008 Certificate Company} New Zealand And Australia Approval Certified This Company Fire Blanket and Ceramic fiber cloth contain absolute amount of binder material which is normally burned at lower temperature and does not affect the insulation property.

Ceramic Cloth is a woven fabric made from high quality alumina silica fiber and especially mechanically needled for increased tensile strength and surface integrity in form of ceramic fiber yarn. It can be used for high temperature applications up to 2300 º F. The cloth is reinforced with fiberglass filament, and optional Inconel/alloy steel wire. Ceramic fiber textiles feature excellent properties of lightweight, low thermal conductivity and chemical stability resisting attack from most corrosive agents. This cloth is widely used in welding, foundry works, aluminum and steel mills, boiler insulation and seal, shipyards, refineries, power plants and chemical plants.

Vermiculite Coated Ceramic Fabric has high vermiculite content of 10 to 12% and provides vital support in the process of collecting molten metal slag. These can be used as an alternative to asbestos based textiles and offers low thermal conductivity as well as superior dielectric strength. Also coming with superior corrosion resistance, these are used at 2300°F / 1260°C continuously, molts above 3000°F / 1650. It is available under part number WCF230V with Roll size of 2.0mmX1mX30m; Weight (kg/roll) of 31kg and Reinforcement of SS304 wire.


  • This fabric has very high vermiculite content (10 to 12%).
  • Allows for collecting molten metal slag.
  • An alternative to asbestos based textiles.
  • Provides low thermal conductivity and good dielectric strength and features excellent corrosion resistance.
  • Used at 2300°F / 1260°C continuously, molts above 3000°F / 1650°C.


  • Industry leading Prices.
  • Premium Quality Products.
  • Products Delivery on Time.

Vermiculite Coated Welding Blanket

Vermiculite Ceramic Fire Blanket Tech Data

  • Brand    : “ Signature ” Powered By Darshan Safety Zone
  • Available Size     : Thickness: 1.5mm To 5.0mm Width :1000mm
  • Place Of Origin : Ahmedabad, India
  • Application         : Use In Welding Blankets, Stress Relieving, Removable Insulation Covers, Fire Blanket, Fire Curtains……
  • Thickness            : 1.5mm,2.0mm,3.0mm
  • Width    : 1000mm Or [Any] Example – 10Met. X 10Met. X 2MM
  • Length  : Roll of 28 to 30 Meters.
  • Chemical Composition   : Al203>48%
  • Working Temperature   : 1260 °C
  • Loss on Ignition L.O.I      : At 850 °C For 50 Minutes
  • Moisture             : At 105 °C For 50 Minutes
  • Melting Point 1720 °C of the Original Fiber Used.
  • Fiber Diameter  : 2-5um
  • Loss on Ignition : <18%
  • Moisture             : <1 %
  • Warp Density     : 48-60 Piece/10cm
  • Weft Density     : 21-30 Piece/10cm
  • Organic Content (%)       : <15
  • Sample Availability          : Yes
  • Delivery Lead Time          : 1 To 2 Days
  • Delivery Terms  : FOB CIF EXW